Anterior and posterior nanohybrid light-cured composite material

  • True reflection of natural teeth, true mimesis, exceptional aesthetic properties Invisible restoration, perfect integration of the composite.
  • Joints cannot be seen
  • Exceptional aesthetic quality after polishing
Reflectys

Demo clip

Samples

Indications

Dental Advisor Reflectys ITENAUniversal composite.
Restoration of both anterior and posterior teeth.

 

  • All classes (I to V)
  • Fractured teeth
  • Restoration of milk teeth

 

"Although I don’t need Dentotemp to hold a temporary for a month, I use it in challenging circumstances, for example for short clinical crowns, bruxing patients, and for deep, destructive bites, such as this patient’s.  And while it does have a high bond strength, it removes easily with minimal cleanup of the preparation." - Dr. Kate Gross

Advantages

  • True reflection of natural teeth, true mimesis, exceptional aesthetic properties
  • Invisible restoration, perfect integration of the composite. Joints cannot be seen
  • Exceptional aesthetic quality after polishing
  • Low polymerization shrinkage: better marginal adaptation
  • Easy handling of the material: ideal texture, does not stick to instruments or gloves, easy to sculpt and quick to polish
  • Remarkable mechanical resistance: enriched with micro-and nano-particles, abrasive resistance for durable restorations
  • No post-operative sensitivity, contains fluoride
  • Radiopacity equivalent to 220% of Aluminium
  • Light-curing
  • Supplied in syringe format or in capsules
  • 16 shades available: A1, A2, A3, A3.5, A4, B1, B2, B3, C2, C3, D3, A20, A30, I, P, E


To know

  • Layer
    • Advised curing time 20s (LED) - 2.5 mm
    • Depth of cure - 2.95 mm
  • Compressive strength - 380 MPa
  • Flexural strength - 170 MPa
  • Flexural modulus - 9110 MPa
  • Film thickness - 8.2 μm
  • Water sorption - 13.66 μg/mm3
  • Solubility - 0.56 μg/mm3
  • Volume shrinkage - 2.37%
  • Radiopacity - 220% of Al

Evaluation of the Reflectys composite from the French laboratory ITENA CLINICAL compared to 3 controls

This study was undertaken at the request of the ITENA CLINICAL company to evaluate the basic properties of the Reflectys composite.

Three experimental approaches were implemented:

  1. Evaluation of its structure by SEM (Scanning Electron Microscopy)
  2. Evaluation of its polishability with a well‐defined SEM instrument sequence
  3. Evaluation of its mechanical properties
    1. Flexion resistance
    2. Micro‐hardness.

Read


Related products

Iperbond Ultra

Universal adhesive

  • Three modes of use : total-etch, self-etch or dual
  • Excellent results: repeatedly reliable bonding to enamel and dentine
  • Low evaporation: no acetone solvent for better consistency

 

 

Luxite

LED curing light

  • 6 curing modes
  • Maximal power 1600mW/cm²
  • 2 years guarantee